17 4 ph stainless steel is a martensitic precipitation hardening stainless steel that provides an outstanding combination of high strength good corrosion resistance good mechanical properties at temperatures up to 600 f 316 c good toughness in both base metal and welds and short time low temperature heat treatments that minimize warpage and scaling.
17 4 ph stainless steel yield strength.
17 4 provides an outstanding combination of high strength good mechanical properties at temperatures up to 600 f 316 c and short duration low temperature heat treatments that minimize warpage and scaling.
Alloy 17 4 is a chromium copper precipitation hardening stainless steel that is used for applications requiring high strength and a moderate level of corrosion resistance.
17 4 ph stainless steel uns s17400 shaped flat square round fine wire plated and bare wire astm a564 astm 693 ams 5523 ams 5604 ams 5643 17 4ph alloy description 17 4 ph is a martensitic chromium nickel copper precipitation hardening stainless steel that provides an.
17 4 ph stainless steel material datasheet typical mechanical properties standard markforged h900 mim h900 astm a564 h900 ultimate tensile strength astm e8 1250 mpa 1190 mpa 1310 mpa 0 2 yield strength astm e8 1100 mpa 1090 mpa 1170 mpa elongation at break astm e8 6 6 10.
It is also known as 630 stainless steel.
It is one of the most widely used precipitation hardening grades as it has high strength hardness up to about 572 f while demonstrating good corrosion resistance in all.
17 7 ph is a chromium nickel aluminum precipitation hardening stainless steel that provides high strength and hardness and a moderate level of corrosion resistance up to 600 f.
17 4 ph stainless steel mechanical properties ak steel 17 4 ph stainless steel provides excellent mechanical properties.
17 4 ph steel contains 4 copper and may be hardened by a single low temperature precipitation hardening heat treatment producing excellent mechanical properties at a high strength level.
17 4 ph provides this high strength in combination with good mechanical properties at temperatures of up to 600 f 316 c.
Tensile strength 231 231 σb mpa yield strength 154 σ 0 2 mpa elongation 56 δ5 ψ ψ akv akv j hbs 235 268 hrc 30.
Tensile strength 115 234 σb mpa yield strength 23 σ 0 2 mpa elongation 65 δ5 ψ ψ akv akv j hbs 123 321 hrc 30 17 4ph mechanical properties.
Type 17 4 is the most common grade of martensitic precipitation hardenable ph alloys.
High strength 17 4 ph stainless steel with a higher chromium content than 15 5 ph stainless steel this high strength 17 4 ph offers better corrosion resistance.
This grade can be easily formed in the austenitic condition similar to type 301 stainless steel and hardened to high strength levels using relatively low heat.